1. Co-dhèanamh ceimigeach:
Tha na h-ìrean alloy de foil alùmanum airson itean iomlaid teas a’ toirt a-steach sa mhòr-chuid 1100, 1200, 8011, 8006, etc. Bho shealladh cleachdadh, chan eil riatanasan teann aig innealan-adhair a thaobh co-dhèanamh ceimigeach itean iomlaid teas alùmanum. Gun làimhseachadh uachdar, 3Tha neart an aghaidh creimeadh math aig A21 alùmanum alloy, feartan meacanaigeach àrd leithid neart agus leudachadh, and high hardness. The choice of alloy depends primarily on the final mechanical properties the material can achieve and the ease of the ant process. Mar eisimpleir, the 1 100 aluminum alloy with higher purity is easier to roll, while the 8011 alloy is more difficult.
2. Mechanical properties:
Mechanical properties mainly refer to the tensile strength, elongation and cupping value of aluminum foil. Bho shealladh cleachdadh, it is hoped that these three indicators are as high as possible, but in terms of the material itself, these three indicators are contradictory, ‘s e sin, when the tensile strength of the aluminum foil is relatively high, the elongation index will decrease; When the elongation of the aluminum foil is increased, the tensile strength will decrease. Uime sin, in practical applications, the intermediate value of the mechanical properties is generally taken, and the specific strength and plasticity values are related to the punching die during the processing of the heat exchange fin. Anns an fharsaingeachd, the punching process of heat exchange fins is divided into two types: stretching type and non-stretching type. The mold for stretch punching requires better plasticity of the aluminum foil, ‘s e sin, the elongation is higher, and the relative strength value can be slightly lower; while the non-stretch mold requires higher strength of the aluminum foil, and plasticity is a secondary indicator. There are many factors affecting the mechanical properties of aluminum foil, mainly the chemical composition and processing technology of aluminum foil. As far as the strength and plasticity of aluminum foil are concerned, by adjusting the chemical composition or changing the processing process and parameters, the plasticity or strength of the material can be changed within a certain range while keeping one side unchanged. 'S e sin ri ràdh, through the adjustment of chemical composition and processing technology, the matching value of aluminum foil strength and plasticity can be changed limitedly.
According to the different requirements for mechanical properties of heat exchange fins, there are currently three main use states of aluminum foil: H22, H24, and H26. Each state corresponds to a certain range of strength and plasticity. Judging from the current situation of the domestic aluminum processing industry, there is no unified standard for the range of mechanical properties of each state. Aig an aon àm, in practical application, the range of mechanical properties of each state is too wide, and the mechanical properties of the product cannot be well controlled to satisfy the user.