アルミ箔のピンホールには主に2つの要因があります, 一つは素材です, もう一つは加工方法です.
1. 不適切な材料と化学組成は、偽アルミ箔のピンホール含有量に直接影響を及ぼします。Fe と Si. 鉄>2.5, Al および Fe の金属間化合物は粗大な化合物を形成する傾向があります。. アルミ箔はカレンダー加工時にピンホールが発生しやすい, FeとSiが相互作用して強固な化合物を形成します. The number of pinholes in 1060 pure aluminum foil is much larger than that in 1035 foil, because the Fe and Si content of 1035 pure aluminum is much higher than that of 1060. But in aluminum foil Ti content >O time. 05, easy to form hard TiB2. The compound is brittle during rolling, which also causes many pinholes. Material surface The horizontal billet surface is scratched, or the surface has severe corrosion spots and metal extrusion. These problems will produce more pinholes or even holes with the thinning of rolling thickness. The material casting process mainly consists of some external particles and dust, as well as bubbles and oxide film. As the rolling thickness becomes thinner, the bubbles are crushed into pinholes, and the oxide film eventually falls off the foil surface, forming pinholes.
2, when the processing method tension is too large, the front slip value is greatly reduced, easy to lead to inconsistency between the roller and aluminum foil. If the aluminum foil surface slips at this time, it will distort the surface and greatly increase the probability of pinhole. There are some small solid particles in the rolling oil, which can easily lead to pinholes in aluminum foil. These particles must be filtered to remove, but in practical filtration, the ash content of the rolled oil tends to exceed a certain range, which can easily lead to pinholes. 加えて, the flow of oil through the filter must be greater than the flow of cooling oil, but in fact, dirty oil often reflux, rolling oil viscosity is too large, eventually make the aluminum foil pockmarked, the rougher the more likely to lead to pinhole.