Wholesale Aluminum foil for capacitor

Hliníková fólia pre kondenzátor

Al kovová zliatina: 1000, 3000, 8000 séria atď
Temperovaný tĺčik: O - H112 atď
šírka: 100mm - 1600mm
Hrúbka: 0.0053mm - 0.2mm
Vnútorný priemer: 76cm, 152cm atď
Materiál jadra: papier, železo, hliník

Aluminum foil for capacitor parameters

Zliatina	Temper	Hrúbka	šírka	Core inner diameter	Maximum outer diameter of aluminum coil	Thickness tolerance	Wettability	Brightness L
Hliníková fólia na kondenzátory 1235	0	0.005-0.016mm	100-500mm	76	500	≦5	Class A (Test kefovou vodou)	≦60

aluminum foil capacitor

The aluminum foil used in electrolytic capacitors is a corrosive material that works under polar conditions. It has higher requirements for the structure of aluminum foil. The aluminum foil used is divided into three types: cathode foil, with a thickness of 0.015mm to 0.06mm; high-voltage foil, with a thickness The thickness is 0.065mm～0.1mm, and the aluminum foil is required to be produced with high-purity aluminum; the thickness of the low-pressure foil is 0.06mm～0.1mm.

Chemical composition of high pressure raw foil and low pressure raw foil（%）
Cu(≤)	Fe(≤)	A(≤)	Al(≥)
0.005	0.003	0.0025	99.99
0.005	0.015	0.015	99.97
0.01	0.02	0.02	99.95
0.01	0.04	0.04	99.93
0.01	0.06	0.06	99.90
0.01	0.10	0.08	99.85
0.0025~0.0050	≤0.014	≤0.014	≥99.97
Note: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Chemical composition of cathode foil（%）
Cu	Fe	A	Al
0.01	0.16	0.16	99.7
0.01	0.25	0.20	99.6
Note: After the agreement between the supplier and the buyer, it can be supplied according to the agreement.

Longitudinal room temperature mechanical properties of aluminum foil

Hrúbka (mm)	Temper	Tensile Strength N /mm2	Elongation δ %
Hrúbka (mm)	Temper	not less than
0.015~0.090	M	24.5	2.0
0.015~0.090	Y	98.0	0.5
0.100~0.200	M	29.4	3.0
0.100~0.200	Y	98.0	0.5

Crystal Structure Properties of Capacitor Aluminum Foil

The average surface dislocation density of the soft-state high-pressure original foil is not more than 10∧6/cm2.
The (100) crystal plane occupancy rate of the soft-state high-pressure original foil is not less than 80%.
The thickness of the oxide film on the surface of the soft-state high-voltage original foil is not more than 6nm.

Note: Foils with other parameters can be supplied by agreement between the supplier and the buyer.

Application

aluminum foil for electrolytic capacitor

Prečo si vybrať nás?

Henan Huawei Aluminium Co., Ltd. je lídrom mnohých výrobcov a dodávateľov hliníka v Číne. Prísne kontrolujeme kvalitu a zameriavame sa na zákazníkov. Dúfame, že s vami budeme mať hĺbkovú spoluprácu a poskytneme vám vysokokvalitné produkty z hliníkového materiálu na mieru OEM služby. Ak chcete získať najnovšie a najlepšie ceny za kg alebo za tonu štandardnej hmotnosti, prosím kontaktujte nás.

Linka na výrobu hliníkových fólií

Balenie

Balíček: Drevené puzdro
Štandardná špecifikácia dreveného puzdra: Dĺžka * Šírka * Výška = 1,4 m * 1,3 m * 0,8 m
Raz potrebné,rozmer dreveného puzdra je možné podľa potreby zmeniť.
Váha brutto hmotnosti na drevené puzdro: 500-700KG Čistá hmotnosť: 450-650KG
Poznámka: Pre špeciálne požiadavky na balenie, zodpovedajúcim spôsobom sa doplnia.