hot ingot rolling
First, kuyeyuka kwa alumini hutupwa kwenye slab, na baada ya homogenization, moto rolling, baridi rolling, annealing ya kati na michakato mingine, inaendelea kuwa baridi iliyokunjwa ndani ya karatasi yenye unene wa karibu 0.4 ~ 1.0 mm kama karatasi tupu. (kutupa → billet inayoviringisha moto → kuviringisha baridi → kuviringisha kwa foil).
Katika ingot moto rolling njia, the hot rolled billet is first milled to remove defects such as oxide layer and impurities on the surface of the ingot, and then homogenized to make the microstructure of the ingot more uniform, followed by hot rolling, cold rolling and intermediate After multiple processes such as annealing, the internal structure uniformity and grain size of the billet have been significantly improved after multiple recovery and recrystallization. Kwa hiyo, the hot-rolled billet is usually of good quality and suitable for high-quality double zero aluminum foil and deep processing. Aluminum foil products. Hata hivyo, in the deep drawing process of hot-rolled billets, there are problems such as high ear rate, easy cracking, and uneven deformation area, which restricts the improvement of the yield of high-quality aluminum foil.
njia ya utupaji roll pacha
Compared with the ingot hot rolling method, the process flow of the aluminum foil blank production by the casting and rolling method is relatively simple; it does not need to go through complicated process steps such as smelting ingot, milling, homogenization and hot rolling, but pours the aluminum melt directly. The two rotating casting rolls (ukungu) are inserted into the casting and rolling area, and the two processes of solidification and hot rolling are simultaneously completed within 2~3s in the casting and rolling area to obtain a plate with a thickness of 4~7mm. Similar to the hot-rolled aluminum foil billet, the cast-rolled sheet also needs to undergo a series of cold rolling and intermediate annealing processes, and finally rolled into a 0.3~0.7mm thick sheet as an aluminum foil billet.